NCM 811

 

NCM 811

 

TOB-NCM811-S

 

Modèl	TOB-NCM% 7b}}S
D50	4.0±1.0
SSA	0.6±0.2
PH	Mwens pase oswa egal a 11.7
OH�% af	Mwens pase oswa egal a 0.30 wt%
CO₃²¯	Mwens pase oswa egal a 0.30 wt%
Kapasite	210% c2�5 mAh/g
Efikasite	89±1 %

 

TOB-NCM% 7b}}C

Modèl	TOB-NCM% 7b}}C
D10	5.0�1.0} um
D50	10.0±2.0 um
D90	20.0±4.0 um
Dmax	Mwens pase oswa egal a 40.0 um
Imidite	Mwens pase oswa egal a 600 ppm
Tape Dansite	Pi gran pase oswa egal a 2.1 g/cm3
SSA	0.6±0.3 m²/g
Dansite Compact	Pi gran pase oswa egal a 3.2 g/cm3
Fe+Cr	Mwens pase oswa egal a 100 ppb
PH	Mwens pase oswa egal a 11.80
OH�% af	Mwens pase oswa egal a 0.40 wt%
CO₃²¯	Mwens pase oswa egal a 0.30 wt%
Kapasite	Pi gran pase oswa egal a 205 mAh/g
Efikasite	Pi gran pase oswa egal a 88%

 

0.1C kapasite espesifik nan NCM811 polymère a se plis pase 200mA-h/g, ki se 30mA-h/g pi wo pase sa yo ki nan NCM523, ak ogmantasyon nan kontni nikèl ak diminisyon nan kontni Cobalt fè NCM811 jwenn debarase m de dilèm pri matyè premyè ki te koze pa sere nan resous Cobalt. Sepandan, LiNiO2 te vin eleman prensipal la nan NCM811, kontablite pou otan ke 70%, epi li dwe prepare nan yon atmosfè oksijèn pi bon kalite asire ke plis nikèl egziste nan +3 valans. Anplis de sa, materyèl la sansib a imidite anbyen, epi li gen tandans fè absòpsyon imidite, kasyon melanje, ak twòp rezidyèl konpoze ityòm sou sifas patikil la pandan pwodiksyon, transfè, depo, ak itilizasyon. Konpoze ityòm rezidyèl sa yo fè pH la pi wo, epi li fasil pou ogmante viskozite sispansyon an pandan batri pulping, e menm vin tankou jele, sa ki fè li difisil pou ajiste sispansyon an ak kouch elektwòd la.

 